YT TORCH MR1800 U shape mosi2 heater molybdenum silicide heater electric heater for industrial oven

Supplier: Yantai Torch Special High Temperature Ceramics Co., Ltd.
Region: Shandong, China
Contact: Ms Eva Wei
Price: $60.00 / >=5 pieces
Min. Order: 5 pieces

Click here to contact

Product details

Color:	Gray;	Voltage:	Custom- made;
After-sales Service Provided:	Video technical support, Online support;	Main application:	Industry Furnace;
Power Source:	Electric;	Condition:	New;
Packaging Detail:	furnace heating element is packed by wooden box;	Brand Name:	YT TORCH;
Shape:	U;	Weight:	Custom- made;
Type:	Air Heater;	Payment Terms:	L/C,T/T;
Place of Origin:	China;	Model Number:	MR1800;
Dimension:	Custom made;	Warranty:	Depend on using condition;
Temperature:	1800C;	Certification:	ISO9000&SGS;
Parameter:	Non-standard custom;	Applicable Industries:	Energy chemical industry;
Material:	MoSi2;	Density:	5.9±0.1;
Diameter:	3/6, 4/9,6/12, 9/18,12/24mm or Custom made;	Dimension(LWH):	Custom- made;

Product Description

Product Name	MR 1800 MoSi2 electric heater
Condition	New	Color	Gray
Place of Origin	Yantai,China(Mainland)	Working Temperature	1000℃-1800℃
Dimension(LWH)	Customized	Power Source	Electric
Power(W)	All Depends	Model Number	MR1800 Type
Density	5.9±0.1g/CM3	Voltage	All Depends
Type	Air Heater	Shape:	U or customized
Brand Name	YT Torch	Weight	All Depends

Properties

Physical Properties

Bulk Density	Bending Strength	Hardness	Water Absorption	Heated Elongation	Fracture Toughness	Compression Strength
≥5.8g/cm³	350MPa	9.9GPa	≤0.2%	≤4%	4.5MPa.m^1/2	650MPa

Chemical Properties

MoSi₂ Heating Element has the ability to withstand oxidation at high temperatures. This is due to the formation of a thin and adhesive protective layer of quartz glass (SiO₂) on the surface. When the element temperature over 1700℃, SiO₂ protective layer which melting point is 1710℃ was fused, and because of the surface tension, it fused into drops, which is useless. However, when element continue working in oxidizing atmospheres, the SiO₂ protective layer is spontaneously rebuilt.

Notice: It is no good to use Molybdenum Disilicide Heating Element for Long-term within a range of 400-700℃, otherwise the element will be powdered by the strong low temperature oxidation..

Indicators in Different Atmospheres

Atmosphere	TC1700	TC1800	MR1800	TC1850
Air	1700	1800	1800	1850
Nitrogen	1600	1700	1700	1750
Argon, Helium	1600	1700	1700	1750
Dry hydrogen, dewpoint -80℃	1150	1150	1150	1200
Moist hydrogen, dewpoint 20℃	1450	1450	1450	1500
Exogas (Ex. 10% CO₂, 5% CO, 15%H₂)	1600	1700	1700	1750
Exogas (Ex. 40% H₂, 20% CO)	1400	1450	1450	1500
Cracked and partially burnt ammonia	1400	1450	1450	1500

Application

How to Assembly

Produce Process

About Us

{ Learn More+ }

1.Product has the capabilities to resistance to oxidation and automatically repair, suitable for continued using in any kinds of oxidizing atmospheres.

2.Product is shaped in hot-working process, which keeps the base material in good tenacity and plasticity at high temperature. The geometrical figure, standard and dimension is canonical, may produce any special shape and any dimension to meet the customer requirement.

3.Because of the special technology, welding spot is firm and shock resistance, which dramatically reduced the damaged probability of welding spot by electric current, as well as transit and installation.

4.High density of YT Torch product increases its electrical conductivity. The characters of faster warming and power consumption low, which reduce production cost.

5.Good appearance quality and tenacity, high mechanical strength.

6.Protective layer of quartz glass is compact and good adhesion with the substrate

7.Excellent high temperature strength which is not easy to deform in use