Silicone bronze welding wire DIN 1733 SG-CuSi3 ERCuSi-A

Supplier: Tongling Hengyuan Welding Materials Co., Ltd.
Region: Anhui, China
Contact: Ms TONGLING HENGYUAN WELDING DAISY
Price: $9.00 / 500 - 1999 kilograms
$7.17 / >=2000 kilograms
Min. Order: 500 kilograms

Click here to contact

Product details

work:	CuSi3	application:	Soldering for copper
Material:	Copper/Copper Alloy, Copper Zinc Bronze,	Packaging Details:	ERCuSn-A electrode, tin bronze wire ERCuSn-A CUSN6: 15kg/reel, 72 reels - 1080kg/pallet 5kg/tube, 1000kg/pallet
place of origin; place of origin:	Anhui, China	Original Equipment Manufacturer:	accept
Flux content:	standard	AWS:	A5.7
Supply capacity:	200 tons per month	diameter:	0.8-6.0mm
weight:	12.5kg/15kg	Custom Support:	OEM, ODM
port:	Shanghai	Melting point:	international standard
product name:	ERCuSn-A SG-CuSi3	brand:	Hengyuan
payment terms:	L/C,D/P,D/A,T/T	model:	ERCuSn-A
Minimum order quantity:	500 kg

Product Description

Product: Silicon Bronze

1. Standard: DIN 1733BS / EN14640 / AWS A5.7

2. Application: Joining and surfacing of copper-zinc alloys and low-copper materials, also suitable for wear-resistant surfacing of low-alloy and non-alloy steels and cast iron MIG surfacing of large workpieces It is recommended to preheat for multi-layer welded steel, Pulse arc welding is recommended. MIG brazing for galvanized sheet.

3. Available size: 0.8mm/0.9mm/1.0mm/1.2mm/1.6mm

4. Packing: 5kg/15kg spool box

Product Description

Silicon bronze

chemical composition(%)

standard

class

alloy

copper

aluminum

iron

manganese

you

phosphorus

lead

silicon

tin

Zinc

other

ISO24373

Copper 6560

CuSi3Mn1

Barr.

0.02

0.5

0.5~

1.5

0.05

0.02

2.8~

4.0

0.2

0.4

0.5

GB/T9460

SCu6560

CuSi3Mn

Barr.

maximum

0.01

maximum

0.5

maximum

1.5

maximum

0.02

2.8~

4.0

maximum

1.0

maximum

1.0

maximum

0.5

BS EN14640

Copper 6560

CuSi3Mn1

Barr.

0.01

0.5

0.5~

1.5

0.02

2.8~

4.0

0.2

0.4

AWS A5.7

C65600

ERCuSi-A

Barr.

0.01

0.05

1.5

0.02

2.8~

4.0

1.0

0.50

DIN 1733

2.1461

SG-CuSi3

Barr.

maximum

0.01

maximum

0.3

0.5~

1.5

maximum

0.02

maximum

0.02

2.8~

4.0

maximum

0.2

maximum

0.2

maximum

0.4

Physical and mechanical properties:

solid temperature

910℃

liquid temperature

1025℃

density

8.5 kg/dm³

tensile strength

330-370N/mm²

elongation

40%

Brinell hardness

80-90HB

introduce:

Most suitable for butt and overlay welding of brass, especially MIG welding of galvanized steel. Preheating is recommended for MIG surfacing of large-size products, and pulse argon arc welding is used for surfacing on steel surfaces.