PE Strange Battery Separator
100% PE material, pocket type
Color: Grey
A battery separator is a polymeric membrane placed between the positively charged anode and negatively charged cathode to prevent an electrical short circuit. The separator is a microporous layer that is moistened by the electrolyte that acts as a catalyst to increases the movement of ions from one electrode to the other electrode.
1. Industrial Separators
Item |
Units |
Parameters |
|
|
|
Standard |
Special |
(B/W) |
mm |
0.300±0.030 |
(0.400~0.600)±0.050 |
(O/A) |
mm |
1.00±0.050 |
(1.00~1.60)±0.080 |
CMDElongation(CMD) |
% |
≥300 |
≥200 |
Electrical Resistance |
Ω.dm2 |
≤0.0015 |
≤ 0.0040 |
Porosity |
% |
≥55 |
≥50 |
B/W oil content |
% |
≥8 |
- |
O/A oil content |
% |
12≤total)≤18 |
15≤(total)≤21 |
Moisture content |
% |
≤3.0 |
≤3.0 |
Dimension stability |
% |
≤1.0 |
≤1.0 |
Acid weight loss |
% |
≤4.0 |
≤4.0 |
Fe content |
% |
≤0.010 |
≤0.015 |
CL content |
% |
≤0.030 |
≤0.030 |
Reducing substance |
ml/g |
≤10 |
≤10 |
2. PE Separators with glass mat
Item |
Units |
Parameters |
||
|
|
PE+GM0.300 |
PE+GM0.600 |
PE+GM0.800 |
(O/A) |
mm |
Standard±0.100 |
Standard±0.100 |
Standard±0.100 |
Laminate Inset from Separator Edge |
mm |
8.0±2.0 |
8.0±2.0 |
8.0±2.0 |
Electrical Resistance |
Ω.dm2 |
≤0.0015 |
≤0.0015 |
≤0.0015 |
Porosity |
% |
≥55 |
≥55 |
≥55 |
Moisture content |
% |
≥4.0 |
≥4.0 |
≥4.0 |
Dimension stability |
% |
≤1.0 |
≤1.0 |
≤1.0 |
Acid weight loss |
% |
≤4.0 |
≤4.0 |
≤4.0 |
Fe content |
% |
≤0.010 |
≤0.010 |
≤0.010 |
CL content |
% |
≤0.030 |
≤0.030 |
≤0.030 |
Reducing substance |
ml/g |
≤10 |
≤10 |
≤10 |
3. Automotive Separators
Item |
Units |
Parameters |
(B/W) |
mm |
0.200±0.030 0.250±0.030 |
(O/A) |
mm |
(0.80~1.30)±0.05 |
Puncture Resistance |
N |
≥8 |
CMD Elongation |
% |
≥300 |
Electrical Resistance |
Ω.dm2 |
≤0.0010(standard) ≤0.0015special) |
Porosity |
% |
≥55 |
B/W oil content |
% |
≥8 |
O/A oil content |
% |
12≤(total)≤18 |
Moisture content |
% |
≤3.0 |
Dimension stability |
% |
≤1.0 |
Wetting time |
S |
≤60 |
Acid weight loss |
% |
≤4.0 |
Fe content |
% |
≤0.010 |
CL content |
% |
≤0.030 |
Reducing substance |
ml/g |
≤10 |
Oxidation stability After-oxidation elongation(CMD) |
% |
≥100(48h) |
4.Motorcycle Separators
Item |
Units |
Parameters |
(B/W) |
mm |
0.200±0.030 0.250±0.030 |
(O/A) |
mm |
(0.60~1.00)±0.05 |
Puncture Resistance |
N |
≥8 |
CMD Elongation |
% |
≥300 |
Electrical Resistance |
Ω.dm2 |
≤0.0010(standard) ≤0.0015(special) |
Porosity |
% |
≥55 |
B/W oil content |
% |
≥8 |
O/A oil content |
% |
12≤(total)≤18 |
Moisture content |
% |
≤3.0 |
Dimension stability |
% |
≤1.0 |
Wetting time |
S |
≤60 |
Acid weight loss |
% |
≤4.0 |
Fe content |
% |
≤0.010 |
CL content |
% |
≤0.030 |
Reducing substance |
ml/g |
≤10 |